| Alloy Steel and Stainless Steel Bolting Materials for High-Temperature Service |
| ASTM A-193 |
B5 |
B6 |
B7 |
B7M |
B8 |
B8M |
B8T |
B16 |
| EQUIVALENCES |
AISI |
501 |
410 |
41/40/42/45 |
41/40/42/45 |
304 |
316 |
321 |
- |
DIN |
12CrMo 19.05 |
X10Cr13 |
42CrMo4 |
42CrMo4 |
X5CrNi 18.09 |
X5CrNiMo 18.10 |
X10CrNiTi 18.09 |
24CrMoV55 |
| CHEMICAL REQUERIMENTS |
(C) Carbon |
>0,10 |
>0,15 |
0,37-0,49 |
0,37-0,49 |
>0,08 |
>0,08 |
>0,08 |
0,36-0,47 |
(Mn) Manganese |
>1 |
>1 |
0,65-1,0 |
0,65-1,0 |
>2 |
>2 |
>2 |
0,45-0,70 |
(P) Phosphorus (máx.) |
0,04 |
0,04 |
0,035 |
0,035 |
0,045 |
0,045 |
0,045 |
0,035 |
(S) Sulfur (max.) |
0.03 |
0,03 |
0,04 |
0,04 |
0,03 |
0,03 |
0,03 |
0,04 |
(Si) Silicon |
>1 |
>1 |
0,15-0,35 |
>1 |
>1 |
>1 |
>1 |
0,15-0,35 |
(Ni) Niquel |
|
|
|
|
8-10,5 |
10-14 |
9-12 |
|
| (Cr) Chromium |
4-6 |
11,5-13,5 |
0,75-1,20 |
0,75-1,20 |
18-20 |
16-18 |
17-19 |
0,80-1,15 |
| (Mo) Molybdenum |
0,40-0,65 |
|
0,15-0,25 |
0,15-0,25 |
|
2-3 |
|
0,50-0,65 |
(V) Vanadium |
|
|
|
|
|
|
|
0,23-0,35 |
(Ti) Titanium (min.) |
|
|
|
|
|
|
5 x C |
|
| MECHANICAL REQUERIMENTS |
| Tensile Strength
(min) |
Lbs/in2 |
100.000 |
110.000 |
125.000 |
100.000 |
75.000 |
75.000 |
75.000 |
125.000 |
| Kg/mm2 |
70,4 |
77,5 |
88 |
70,4 |
52,8 |
52,8 |
52,8 |
88 |
| Yield Strength (min) |
Lbs/in2 |
80.000 |
85.000 |
105.000 |
80.000 |
30.000 |
30.000 |
30.000 |
105.000 |
| Kg/mm2 |
70,4 |
77,5 |
88 |
70,4 |
52,8 |
52,8 |
52,8 |
88 |
| Elong. (%) (min.) |
16 |
15 |
16 |
18 |
30 |
30 |
30 |
18 |
| Reduct. % (min.) |
50 |
50 |
50 |
50 |
50 |
50 |
50 |
50 |
| RECOMMENDED SERVICE TEMPERATURE SERVICE |
| (Min) |
- |
- |
-45ºC |
- |
-198ºC |
-198ºC |
-198ºC |
-29ºC |
| (Max) |
- |
- |
482ºC |
- |
675ºC |
675ºC |
675ºC |
575ºC |
|
|